Technical Data:
Typical analysis ppm. Ag 500,Bi<10,Pb<50,O 500, other metals <300

Technical Data:
POA = Price on application. Copper flat sheet max size 600mm x 1200mm. Electrical conductivity at 20°C % IACS (mass) annealed min 98.3%. EN1652 CW008A HO65. Tensile strength 253 N/mm2. 0.2% proof strength 172 N/mm2. Elongation 40%. Hardness HV0.5 77. Thickness : min 0.295mm, Max 0.305mm. Tolerance on thichness ±0.005mm. Surface finish sampling length 0.8mm: Trans 0.1 Ra (µm) Long 0.084Ra (µm) Typical analysis ppm: Bi 5, Pb 50, O< 5. Cu + Ag min 99.99%,

Technical Data:
POA = Price on application. FLAT sheet. Maximum size 600mm x 1200mm Typical analysis ppm: Ag 500, Bi< 10, Pb< 50, O 400, other metals < 300.

Technical Data:
POA = Price on application. Copper flat sheet max size 600mm x 1200mm. Electrical conductivity at 20°C % IACS (mass) annealed min 100%. EN1652 CW008A HO65. Tensile strength 237 N/mm2. 0.2% proof strength 190 N/mm2. Elongation 20%. Hardness HV2 84. Thickness : min 0.393mm, Max 0.401mm Average 0.397mm. Tolerance on thichness ±1.6%. Surface finish sampling length 0.8mm: Trans 0.092 Ra (µm) Long 0.046 Ra (µm) Typical analysis ppm: Bi 5, Pb 50, O< 5. Cu + Ag min 99.99%,

Technical Data:
Typical analysis ppm: Ag 500, Bi< 10, Pb< 50, O 400, other metals < 300.

Technical Data:
Typical analysis ppm:P<3,S<15,Zn<1,Cd<1,0<5,Hg<1,Bi<10,Pb<10,Se<10,Te<10, O <20,(Bi+Sn+Mn+Sb+As+Se+Te total 40 max), Balance Cu 99.98+%.

Technical Data:
POA = Price on application. Finish 2B plastic coated both sides. Maximum size 500mm x 1000mm. Analysis maximum %: C 0.06%, Mn 2.0%, P 0.040%, S 0.015%, Si 0.75%, Cr 17.0-19.0%, Ni 9.0-11.0%, Ti > 5 x (C + N), N 0.10% balance Fe.

Technical Data:
Maximum size 610mm x 914mm. Chemical composition to ASTM A 753-97 Alloy 4 and MIL-N-14411C composition 1. After forming or machining, final annealing is generally required to increase grain structure, which improves shielding efficiency. Batch No. Gi4085 Actual Analysis ppm: C 30, Mn 5000, Si 2200, S 10, P 50, Ni 80.1%, Cr 500, Mo 4.6%, Cu 100, Co 400, Fe Balance

Technical Data:
Maximum size 610mm x 762mm. Chemical composition to ASTM A 753-97 Alloy 4 and MIL-N-14411C composition 1. Material is annealed in increase grain size which improves shielding efficiency Batch No. Gi4084 Actual Analysis ppm: C 30, Mn 4900, Si 2100, S <10, P <30, Ni 80.1%, Cr 400, Mo 4.7%, Cu 100, Co 800, Fe Balance

Technical Data:
POA = Price on application. Tolerance on thickness ±0.050mm. Maximum size 762mmx1010mm. Chemical composition to ASTM A753 - 08 (2013) UNS N14080. Material is annealed in increase grain size which improves shielding efficiency Typical mechanical properties: Hardness value 160HV. Grain size 8. Tensile strength 700 MPa. Elongation 35%. Typical analysis ppm:Ni 80-81%, Mo 4.5-6%, Si 500-4000, Mn 0-5000, C 100, balance Fe.