Technical Data:
Gi4913 Tension levelled. Surface finish 1BA. Tensile strength 645 MPa. Yield strength 0.2% offset 285 MPa. AISI 316 L (AMS 5524L R2-14) (AMS-5507G) (ASTM-A-240-15B) (ASTM-A-666-15) (ASME-SA-240 ED 2015) Hardness value 81 HRBW. Elongation 68.0%. ASTM grain size 8. Surface finish =0.162 Ra (µm). DFARS compliant. Actual analysis Gi4913 ppm: C 200, Mn 1.65%, P 330, S 4, Si 3400, Cr 16.82%, Ni 10.02%, Mo 2.05%, Cu 4300, N 400, Co 2600. Fe Balance.

Technical Data:
Typical analysis ppm: C<300, Si<1%, Mn<2%, Ni 10-14%, Cr 16-18%, Mo 2-3%, S<300, P<450, Fe balance.

Technical Data:
POA = price on application. Batch #Gi4651 Tensile strength 660 MPa. Yield strength 0.2% 333 MPa.Elongation 60.0%. Tolerance on thickness ±0.025mm. (AMS 5507G) (AMS 5524L R1014) (ASTM-A-240-15B) (ASTM-A-666-15) (ASME-SA-240 ED 2015) AISI316 L Grain size 8 ASTM. Surface finish, sampling length 0.8mm T 0.047 - 0.086 Ra(µm) L 0.058 - 0.064 Ra(µm). Finish 1BA. Annealed. Hardness value 83 HR15TW. Actual analysis batch #Gi4651 ppm: C 220, Mn 1.64%, P 330, S 5, Si 3300, Cr 16.68%, Ni 10.13%, Mo 2.04%, Cu 4300, N 400, Co 2800. Fe Balance.

Technical Data:
POA = Price on application. Finish 2B Plastic coated both sides Typical analysis ppm: C<300, Si<1%, Mn<2%, Ni 10-14%, Cr 16-18%, Mo 2-3%, S<300, P<450, Fe balance.

Technical Data:
Typical analysis ppm: C<300, Si<1%, Mn<2%, Ni 10-14%, Cr 16-18%, Mo 2-3%, S<300, P<450, Fe balance.

Technical Data:
Finish 2B (specification EN10088 1.404 equivalent to AISI316L) Typical analysis ppm: C<300,Si<1%,Mn <2%,Ni10-14%,Cr16-18%,Mo 2-3%,S<300,P<450, Fe balance.

Technical Data:
Gi4599 Tension levelled. Tensile strength 668 MPa. Yield strength 0.2% 296 MPa. Elongation 62.0%. Surface finish 0.234 Ra(µm). Finish 2D. Annealed pickled.(AMS 5510S) Actual analysis Gi4599 ppm: C 101, Mn 1.469%, P 290, S 10, Si 4195, Cr 17.1475%, Ni 9.03%, Mo 2005, Cu 3055, N 125, Ti 1770, Pb 10. Fe Balance.

Technical Data:
Tension levelled. Price on application. Batch #Gi4650 Tension levelled. Tensile strength 613 MPa. Yield strength 0.2% 283 MPa. Elongation 60.0%. Finish 1BA. Annealed. (AMS 5510S) (ASME-SA-240 ED 20100 (ASTM A 240 16) Heat #836013. AISI 321 Grain size 10.0 Tolerance on thicknness ± 0.025mm. Surface finish, sampling length 0.8mm, T 0.076 - 0.188 Ra (µm), L 0.731 - 0.082 Ra (µm) Hardness value 172 HV1Kg. Actual analysis batch # Gi4650 ppm: C 100, Mn 1.79%, P 250, S 1, Si 5400, Cr 17.30%, Ni 9.18%, Mo 2700, Cu 3800, N 100, Ti 1600, Co 2300. Fe Balance.

Technical Data:
POA = Price on application. Finish 2B plastic coated both sides. Maximum size 500mm x 1000mm. Analysis maximum %: C 0.06%, Mn 2.0%, P 0.040%, S 0.015%, Si 0.75%, Cr 17.0-19.0%, Ni 9.0-11.0%, Ti > 5 x (C + N), N 0.10% balance Fe.

Technical Data:
Material is magnetic (Ferritic grade) Typical analysis maximum: C 800, Si 1%, Mn 1%, Ni 1%, Cr 16-18%, P 400, S 300, Fe balance.