Technical Data:
Typical analysis ppm: Cr 17-20%, Mn<2%, Ni 8-11%, C<300, Fe balance.

Technical Data:
Low carbon, vacuum melted Medical grade ASTM F138-13, ISO 5832-1-2007. Batch Gi4326 Break Load 0.743Kg, Tensile Strength 1583 MPa, Elongation 1.9%, Yield Load 0.697Kg, Yield Strength 1486MPa. Diameter tolerance (+0.0025mm - 0.0026mm), Grain size 8.5 (per ASTM E112). Actual analysis Gi4326 ppm: C 190, Mn 1.51%, P 190, S 30, Si 3700, Cr 17.39%, Ni 14.17%, Mo 2.78% N 370, Cu 3600, Fe Balance. (3.3xMo) + Cr=26.564%.

Technical Data:
Low carbon, Vacuum melted Medical grade ASTM F138, ISO 5832-1:Composition D-2007 Batch Gi4327 Break Load 0.370Kg, Tensile Strength 799 MPa, Elongation 34%, Yield Load 0.263Kg, Yield Strength 567 MPa. Diameter tolerance (+0.0025mm - 0.0026mm), Grain size 5 (per ASTM E112). Actual analysis Gi4327 ppm: C 160, Mn 0.40%, P 130, S 20, Si 4700, Cr 17.33%, Ni 13.70%, Mo 2.81% N 340, Cu 900, Fe Balance. (3.3xMo) + Cr=26.603%.

Technical Data:
Batch No. B/1 Actual diameter 0.154mm - 0.155mm. Typical analysis ppm: Cr 16.5 - 20%,Mn<2%,Ni 8-14%,C<1200, Mo 2.5 - 3%,Fe balance.

Technical Data:
Low carbon. Vacuum melted. Medical grade ASTM F138 & ISO 5832-1 Batch Gi4097 Break Load 2.87 Kg, Tensile strength 1598 MPa, Elongation 2.5%, Yield load 2.55Kg, Yield strength 1418 MPa. Actual analysis Gi4097 ppm: C 210, Mn 1.68%, P 160, S 10, Si 4600, Cr 17.52%, Ni 14.82%, Mo 2.73%, N 200, Cu 1300, Fe Balance. (3.3xMo) + Cr=26.529%

Technical Data:
Typical analysis ppm: Cr 16.5-20%, Mn<2%, Ni 8-14%, C<1200, Mo 2.5-3%, Fe balance.

Technical Data:
Typical analysis ppm: C<300, Si <1%, Mn <2%, Ni 10-14%, Cr 16-18%, Mo 2-3%, S <300, P <450, Fe balance.

Technical Data:
AISI 316 - DIN 1.4401 Gi2875 Tensile strength 1522 -1606 MPa. Elongation 4%. EN10270-3:2001 1.4401 (was BS 2056 316S42) Actual analysis Gi2875 ppm: C 460, Si 3900, S 10, P 280, Mn 1.42%, Ni 10.58%, Cr 17.72%, Mo 2.03%. Fe balance.

Technical Data:
Tolerance on length ±0.5mm, bow ±0.025mm. Low carbon. Vacuum melted. Medical grade ASTM F138 & ISO 5832-1 Batch Gi4096 Break Load 2.87 Kg, Tensile strength 1598 MPa, Elongation 2.5%, Yield load 2.55Kg, Yield strength 1418 MPa. Actual analysis Gi4096 ppm: C 210, Mn 1.68%, P 160, S 10, Si 4600, Cr 17.52%, Ni 14.82%, Mo 2.73%, N 200, Cu 1300, Fe Balance. (3.3xMo) + Cr=26.529%

Technical Data:
Reels of length 5m, 25m & 100m only. Insulated wire batch No. Gi4387. Bare wire low carbon, vacuum melted Medical grade ASTM F138, ISO 5832-1:Composition D-2007 Bare wire batch No. Batch Gi4327 Break Load 0.370Kg, Tensile Strength 799 Mpa, Elongation 34%, Yield Load 0.263Kg, Yield Strength 567 MPa. Actual analysis Gi4327 ppm: C 160, Mn 0.40%, P 130, S 20, Si 4700, Cr 17.33%, Ni 13.70%, Mo 2.81% N 340, Cu 900, Fe Balance.