FE6304
Stainless Steel AISI 316L Wire
- Composition:
- Fe/Cr18/Ni10/Mo3 (Low Carbon)
- Diameter:
- 0.15 mm
- Description:
- Temper hard Vacuum Melted.
Technical Data:
Low carbon. Vacuum melted. Medical grade ASTM F138 & ISO 5832-1 Batch Gi4097 Break Load 2.87 Kg, Tensile strength 1598 MPa,... Low carbon. Vacuum melted. Medical grade ASTM F138 & ISO 5832-1 Batch Gi4097 Break Load 2.87 Kg, Tensile strength 1598 MPa, Elongation 2.5%, Yield load 2.55Kg, Yield strength 1418 MPa. Actual analysis Gi4097 ppm: C 210, Mn 1.68%, P 160, S 10, Si 4600, Cr 17.52%, Ni 14.82%, Mo 2.73%, N 200, Cu 1300, Fe Balance. (3.3xMo) + Cr=26.529%