FE6214
Stainless Steel AISI 316L Wire
- Composition:
- Fe/Cr18/Ni10/Mo3 (Low Carbon)
- Diameter:
- 0.075 mm
- Description:
- Temper annealed Vacuum melted. Finish Bright.
Technical Data:
Low carbon, Vacuum melted Medical grade ASTM F138, ISO 5832-1:Composition D-2007 Batch Gi4327 Break Load 0.370Kg, Tensile Strength... Low carbon, Vacuum melted Medical grade ASTM F138, ISO 5832-1:Composition D-2007 Batch Gi4327 Break Load 0.370Kg, Tensile Strength 799 MPa, Elongation 34%, Yield Load 0.263Kg, Yield Strength 567 MPa. Diameter tolerance (+0.0025mm - 0.0026mm), Grain size 5 (per ASTM E112). Actual analysis Gi4327 ppm: C 160, Mn 0.40%, P 130, S 20, Si 4700, Cr 17.33%, Ni 13.70%, Mo 2.81% N 340, Cu 900, Fe Balance. (3.3xMo) + Cr=26.603%.