FE6317
Stainless Steel AISI 316L Fil Isolé - Longueurs de Coupe Droite
- Diamètre du fil nu:
- 0,075 mm
- Composition:
- Fe/Cr18/Ni10/Mo3 (Low Carbon)
- Épaisseur du revêtement:
- 0,018 mm
- Diamètre Extérieur:
- 0,112 mm
- La Description:
- Temper annealed Vacuum Melted. Quadruple PTFE insulated.
- Remarque:
- Tous les poids indiqués sont des poids de fil nu.
Données techniques:
POA = Price on Application. Tolerance on length ±0.5mm. Bow 0.25mm . Bare wire low carbon, vacuum melted Medical grade ASTM F138,... POA = Price on Application. Tolerance on length ±0.5mm. Bow 0.25mm . Bare wire low carbon, vacuum melted Medical grade ASTM F138, ISO 5832-1:Composition D-2007 Bare wire batch No. Batch Gi4327 Break Load 0.370Kg, Tensile Strength 799 MPa, Elongation 34%, Yield Load 0.263Kg, Yield Strength 567 MPa. Actual analysis Gi4327 ppm: C 160, Mn 0.40%, P 130, S 20, Si 4700, Cr 17.33%, Ni 13.70%, Mo 2.81% N 340, Cu 900, Fe Balance. (3.3xMo) + Cr=26.603%.