Molybdenum Foil

2339 (2)

Product Line MO1821

0.025 mm (thickness). Purity 99.95%. Temper annealed, Quality - Not Light Tight

item no
Weight/pc (g)DimensionsQuantityPrice in
US dollars
Add to
MO1821010.1600.025 x 25 x 25mm1pc$114.00 Add to order
MO182104"0.025 x 25 x 25mm10pcs$213.00 Add to order
MO1821090.6390.025 x 50 x 50mm2pcs$168.00 Add to order
MO182111"0.025 x 50 x 50mm10pcs$299.00 Add to order
MO1821152.560.025 x 100 x 100mm1pc$195.00 Add to order
MO182116"0.025 x 100 x 100mm2pcs$244.00 Add to order
MO182117"0.025 x 100 x 100mm5pcs$346.00 Add to order
MO182118"0.025 x 100 x 100mm10pcs$469.00 Add to order
MO1821225.750.025 x 150 x 150mm1pc$249.00 Add to order
MO182123"0.025 x 150 x 150mm2pcs$321.00 Add to order
MO182124"0.025 x 150 x 150mm5pcs$585.00 Add to order
MO182125"0.025 x 150 x 150mm10pcs$894.00 Add to order
MO18212610.220.025 x 200 x 200mm1pc$302.00 Add to order
MO182127"0.025 x 200 x 200mm2pcs$432.00 Add to order
MO182128"0.025 x 200 x 200mm5pcs$617.00 Add to order
MO182132230.025 x 300 x 300mm1pc$470.00 Add to order
MO182133"0.025 x 300 x 300mm2pcs$857.00 Add to order
MO18213638.30.025 x 150mm Coil1mPOAPlease contact us
MO18214079.20.025 x 310mm Coil1mPOAPlease contact us
Not Light Tested (NLT) may not be free from pinholes. POA = Price on application.
Batch #Gi2861 Tensile Strength 1052.8 MPa, Tensile yield strength 1043.2 MPa Tensile elongation 1.30% Tensile strength transverse 1056.3 MPa Tensile yield strength 1050.1 MPa Tensile elongation 0.60%. Batch #Gi2861 actual analysis ppm: Al 10, Ca 10, C 30, Cr 10, Cu 10, Fe 10, Pb 10, Mg 10, Mn 10, Ni 10, Si 10, Sn 10, Ti 10. Balance Mo>99.95%


Advent Research Materials Product Catalogue

Download the Catalogue

You can download our entire product catalogue to your desktop. Available in five currencies and updated daily.

Download here »

Periodic Table Poster by Advent Research Materials

Periodic Table Poster

Purchase Advent's stylish periodic table poster containing detailed information for every element.

Buy here »

Go back »